We are serving nearly 200 products in all major categories like Austhenitic Stainless Steel, Super Austhenitic Stainless Steel, Duplex Steel, High Nickel Alloys, Martensic Steel, Ferretic Steel ,Rare base metals & non Ferrous Products
| INCONEL ® Alloy |
| Inconel alloy Products |
|
| Inconel alloy Grades |
- Inconel 600: Solid solution strengthened
- Inconel 625: Acid resistant, good weldability
- Inconel 690: Low cobalt content for nuclear applications, and low resistivity
- Inconel 718: Gamma double prime strengthened with good weldability
- Inconel 751: Increased aluminum content for improved rupture strength in the 1600°F range
- Inconel 792: Increased aluminum content for improved high temperature corrosion properties, used especially in gas turbines
- Inconel 939: Gamma prime strengthened with good weldability
|
| Melting Point |
2,500°F (1,372°C) |
| Characteristics |
- Nickel-Chromium-Iron alloy
- Resists corrosion and heat
- High strength and good workability
- Virtually immune to chloride-ion stress-corrosion cracking
- Not hardened by precipitation
- Resistant to sulfur compounds
- Resistant to oxidizing conditions at high temperatures
|
| |
| Chemical Composition |
| Nickel (plus Cobalt) |
72.0% min |
| Chromium |
14 - 17% |
| Iron |
6 - 10% |
| Carbon |
0.15% max |
| Manganese |
1.0% max |
| Sulphur |
0.015% max |
| Silicon |
0.50% max |
| Copper |
0.50% max |
| |
| Physical Properties |
| Density |
0.304 lb/cu in (8.43 gm/cu cm) |
| Specific Heat |
0.106 (at 70deg;F, Btu/lb/ °F) |
| Poisson's Ratio |
0.29 (at 70°F) |
| Electrical Resistivity |
620 (at 70°F, ohm/circ mil/ft) |
| Curie Temperature |
192°F |
| Permeability |
1.010 (at 70°F and 200 oersted) |
| Thermal Conductivity |
103 (Btu in/ft2 h °F)) |
| |
| Application |
- Heat treating industry for retorts, muffles, roller hearths, and other furnace components for heat-treating baskets and trays
- Aeronauts industry
- Electronics industry
- Nuclear reactors
|